球状超细高纯碳化钛应用实例-烧结活性

时间:2019-05-16 14:55 作者:长玉特陶

球状超细高纯碳化钛应用实例

Application of Spherical Super-fine High Purity Titanium Carbide

——烧结活性
——Sintering Activity

球状超细高纯碳化钛性质

Properties of Spherical Super-fine High Purity Titanium Carbide


C total  min. 19.4wt. %
C free   max. 0.2wt. %
O          max. 0.9wt.%
N          max. 0.02wt. %
Fe         max. 0.015wt. %
Ca         max. 0.02wt. %
Si          max. 0.02wt. %

应用实例——热压烧结TiC陶瓷

Application Example——Hot-pressed TiC ceramics

采用传统的热压烧结工艺
Conventional process for hot pressing sintering


应用实例——热压烧结TiC陶瓷

Application Example——Hot-pressed TiC ceramics

结论

Conclusion

通过采用球状超细高纯碳化钛粉体,可大幅降低陶瓷产品的烧结温度,从而细化晶粒,提高力学性能。 
The sintering temperature of the ceramic product can be greatly reduced, thereby refining the crystal grains and improving the strength by using spherical super-fine high purity TiC powders.

                                              